Hardfacing Welding Electrodes

Hardfacing anode of the rapid steel for fix welding of cutting apparatuses, drills, stepping machines and so forth. The weld metal acquires its most extreme hardness by twofold treating. Reasonable for step welding. To stay away from issues with breaking, the working temperature ought to be preferrably 400-500°C.

Slider

Hardfacing Welding Electrodes

Technical Detail

Product Name Classification Mechanical Properties Of Weld Metal (Typical) Unique Feature(All Vaccum Packed) TDS
AWS/SFA Yield Strength N/mm2 Tensile Strength N/mm2(MIN) Elongation 4D(%) Impact (J) Welding Conditions
HARDFACING WELDING ELECTRODES
1 GM 25R DIN 8555: E1-UM-250         AC;DC+ Hardness : 250-300 BHN Rutile Type Download
2 GM 35 DIN 8555: E1-UM-350 AC;DC+ Hardness : 37-40 Hrc Rutile Type Download
3 GM 40 DIN 8555: E7-UM-200KP AC;DC+ Heavy basic coated austenitic manganese alloyed electrode. Hardness as welded : 180-220 (BHN) Hardness (work condition) : 400-450 (BHN) Download
4 GM MN DIN 8555: E7-UM-200KP AC;DC+ Heavy basic coated austenitic manganese alloyed electrode. Hardness as welded : 170-220 (BHN) Hardness (work condition) : 400-500 (BHN) Download
5 GM HARD DIN:8555: E6-UM-55P AC;DC+ 500 -550 BHN (Basic Coated Electrdoe depositing alloy cast iron which is hard and extremly resistant for metal to metal wear. Download
6 GM 50 R DIN:8555: E6-UM-60P AC;DC+ Hardness : 57-60 HRc Basic Coated. Download
7 GM 55R DIN:8555: E6-UM-60P AC;DC+ Hardness : 57-60 HRc Rutile Type. Download
8 GM 60 R DIN:8555: E6-UM-60-S AC;DC+ Hardness : 58-60 HRc Rutile Type. Download